ABSTRACT Objective This in situ/ex vivo study investigated the effect of CO2 laser irradiation and acidulated phosphate fluoride gel (APF) application, separately and in combination, on enamel resistance to erosion. Material and Methods During 2 experimental 5-day crossover phases, 8 volunteers wore intraoral appliances containing bovine enamel blocks which were submitted to four groups: 1st phase - control, untreated and CO2 laser irradiation, 2nd phase - fluoride application and fluoride application before CO2 laser irradiation. Laser irradiation was performed at 10.6 µm wavelength, 5 µs pulse duration and 50 Hz frequency, with average power input and output of 2.3 W and 2.0 W, respectively (28.6 J/cm2). APF gel (1.23%F, pH 3.5) was applied on enamel surface with a microbrush and left on for 4 minutes. Then, the enamel blocks were fixed at the intraoral appliance level. The erosion was performed extraorally 4 times daily for 5 min in 150 mL of cola drink. Enamel loss was measured profilometrically after treatment and after the in situ phase. The data were tested using one-way Repeated Measures Anova and Tukey's test (p<0.05). Results CO2 laser alone (2.00±0.39 µm) did not show any significantly preventive effect against enamel erosion when compared with the control group (2.41±1.20 µm). Fluoride treated enamel, associated (1.50±0.30 µm) or not (1.47±0.63 µm) with laser irradiation, significantly differed from the control. Conclusion The APF application decreased enamel wear; however, CO2 laser irradiation did not enhance fluoride ability to reduce enamel wear.

OBJECTIVE: This in situ study evaluated the discriminatory power and reliability of methods of dental plaque quantification and the relationship between visual indices (VI) and fluorescence camera (FC) to detect plaque. MATERIAL AND METHODS: Six volunteers used palatal appliances with six bovine enamel blocks presenting different stages of plaque accumulation. The presence of plaque with and without disclosing was assessed using VI. Images were obtained with FC and digital camera in both conditions. The area covered by plaque was assessed. Examinations were done by two independent examiners. Data were analyzed by Kruskal-Wallis and Kappa tests to compare different conditions of samples and to assess the inter-examiner reproducibility. RESULTS: Some methods presented adequate reproducibility. The Turesky index and the assessment of area covered by disclosed plaque in the FC images presented the highest discriminatory powers. CONCLUSION: The Turesky index and images with FC with disclosing present good reliability and discriminatory power in quantifying dental plaque.

Studies have shown the cariostatic effect of Er,Cr:YSGG (2.78 mm) laser irradiation on human enamel and have suggested its use on caries prevention. However there are still no reports on the intrapulpal temperature increase during enamel irradiation using parameters for caries prevention. The aim of this in vitro study was to evaluate the temperature variation in the pulp chamber during human enamel irradiation with Er,Cr:YSGG laser at different energy densities. Fifteen enamel blocks obtained from third molars (3 x 3 x 3 mm) were randomly assigned to 3 groups (n=5): G1 - Er,Cr:YSGG laser 0.25 W, 20 Hz, 2.84 J/cm², G2 - Er,Cr:YSGG laser 0.50 W, 20 Hz, 5.68 J/cm², G3 - Er,Cr:YSGG laser 0.75 W, 20 Hz, 8.52 J/cm². During enamel irradiation, two thermocouples were fixed in the inner surface of the specimens and a thermal conducting paste was used. One-way ANOVA did not show statistically significant difference among the experimental groups (a=0.05). There was intrapulpal temperature variation <0.1ºC for all irradiation parameters. In conclusion, under the tested conditions, the use of Er,Cr:YSGG laser with parameters set for caries prevention lead to an acceptable temperature increase in the pulp chamber.

Este estudo in vitro avaliou a resistência ao cisalhamento da dentina submetida ao tratamento com dois agentes clareadores contendo peróxido de carbamida a 10% depois de 15 dias de clareamento e armazenagem em saliva artificial. Fragmentos de dentina foram aleatoriamente distribuídos em 3 grupos (n = 20) para receber o tratamento com dois diferentes agentes clareadores (Rembrandt a 10% ou Opalescence a 10%) ou com um agente placebo, aplicados na superfície dental por 8 horas diárias. No restante do tempo, os espécimens permaneceram imersos em saliva artificial. Após o tratamento por 42 dias, os fragmentos foram armazenados em saliva artificial por 14 dias. Outro grupo (n = 20) somente recebeu a aplicação de água destilada e deionizada por 56 dias. Um sistema adesivo e uma resina composta microhíbrida foram utilizados para o preparo dos corpos-de-prova para o teste de cisalhamento. Após os ensaios, a superfície foi examinada visualmente com um estereoscópio com aumento de 30 X. A análise de variância (ANOVA) e o teste SIDAK mostraram que a dentina tratada com Opalescence a 10% apresentou maiores valores de resistência ao cisalhamento do que a tratada com o Rembrandt a 10% ou com o agente placebo. Os grupos tratados com Rembrandt a 10%, Opalescence a 10% ou agente placebo não diferiram do grupo que recebeu somente o tratamento com água destilada e deionizada. Agentes clareadores contendo peróxido de carbamida a 10% ou um agente placebo não alteraram a resistência ao cisalhamento da dentina após 15 dias de imersão em saliva artificial.

This in vitro study evaluated the shear bond strength (SBS) of dentin treated with two 10% carbamide peroxide bleaching agents 15 days after bleaching and storage in artificial saliva. Dentin fragments were randomly divided into 3 groups (n = 20) for the treatment with the two different bleaching agents (Rembrandt 10% or Opalescence 10%) or with a placebo agent, applied to the tooth surface for 8 hours a day. During the remaining time, the specimens were stored in artificial saliva. After 42 days, the fragments were stored in artificial saliva for 14 days. Another group (n = 20) was exposed to distilled and deionized water for 56 days. An adhesive system and microhybrid composite resin were used to prepare specimens for the SBS test. SBS tests were performed and the fractured surfaces were visually examined using a stereoscope at 30 X magnification. The analysis of variance (ANOVA) and SIDAK tests showed higher SBS values for dentin treated with Opalescence 10% than for dentin treated with Rembrandt 10% or placebo. Groups treated with Rembrandt 10%, Opalescence 10% or placebo did not differ from the group treated with distilled and deionized water. Ten percent carbamide peroxide agents or a placebo agent caused no differences in SBS of dentin after 15 days of storage in artificial saliva.